Barka da zuwa gidajen yanar gizon mu!
FeCrAl 0cr23al5 dumama element flat waya & tsiri ta masana'anta
FeCrAl 0cr23al5 dumama element lebur waya &tsirita masana'anta
| Daraja | 0Cr23Al5 |
| Girman | kauri: 0.05-3mm nisa: 4-250mm |
| Surface | tsaga mai haske |
| Nauyi | 1-3kg / yi, bisa ga abokan ciniki' yawa |
| Resistivity | 1.3±0.05μΩ.m |
| Hardness (HV) | Saukewa: 180-210HV |
| Tsawaitawa | ≥16% |
| Daraja | Mafi girman zafin jiki | Resistivity | Tauri | Ƙarfin ƙarfi | Tsawaitawa |
| 0Cr13Al4 | 1050 ℃ | 1.25± 0.05μΩ.m | Saukewa: 180-210HV | ≥550N/mm2 | ≥16 |
| 0Cr15Al5 | 1100 ℃ | 1.3±0.05μΩ.m | Saukewa: 180-210HV | ≥550N/mm2 | ≥16 |
| 0Cr21Al6Nb | 1300 ℃ | 1.42± 0.05μΩ.m | 200-240HV | 750N/mm2 | ≥12 |
| Cr20Ni80 | 1200 ℃ | 1.09± 0.05μΩ.m | Saukewa: 180-220HV | 750N/mm2 | ≥20 |
| Cr15Ni60 | 1150 ℃ | 1.12± 0.05μΩ.m | Saukewa: 175-210HV | 750N/mm2 | ≥20 |
| Cr20Ni35 | 1100 ℃ | 1.04± 0.05μΩ.m | Saukewa: 180-220HV | 750N/mm2 | ≥20 |
| Cr25Ni20(310S) | 1100 ℃ | 0.86± 0.05μΩ.m | Saukewa: 180-220HV | 750N/mm2 | ≥20 |
| Daraja | Abubuwan sinadaran% | ||||||||
| C | P | S | Mn | Si | Cr | Ni | Al | Fe | |
| ≤ | |||||||||
| 0Cr15Al5 | 0.04 | 0.02 | 0.01 | 0.3 | ≤0.5 | 13-14 | 1 | 4.8-5.0 | daidaitawa |
| 0Cr21Al6Nb | 0.05 | 0.025 | 0.02 | 0.5 | ≤0.6 | 21-23 | ≤0.6 | 5-7 | daidaitawa |
| 0Cr13Al4 | 0.04 | 0.02 | 0.01 | 0.3 | ≤0.5 | 13-14 | 1 | 4.8-5.0 | daidaitawa |
| Cr20Ni80 | 0.08 | 0.02 | 0.015 | 0.6 | 0.75-1.6 | 20-23 | daidaitawa | 0.5 | ≤1.0 |
| Cr15Ni60 | 0.08 | 0.02 | 0.015 | 0.6 | 0.75-1.6 | 15-18 | 55-61 | 0.5 | daidaitawa |
| Cr20Ni35 | 0.08 | 0.02 | 0.015 | 1.0 | 1-3 | 18-21 | 34-37 | - | daidaitawa |
| Cr25Ni20 | 0.08 | 0.045 | 0.03 | 2.0 | 0.4-0.6 | 24-26 | 19-22 | - | daidaitawa |
Shanghai Tankii Alloy Material Co., Ltd.mayar da hankali a kan samar da nichrome gami, thermocouple waya, fecral gami, daidai alloy, jan nickel gami, thermal fesa gami da dai sauransu a cikin nau'i na waya, takardar, tef,tsiri, sanda da faranti.
Mun riga mun samu ISO 9001 ingancin tsarin takardar shaidar da yarda da ISO 14001 muhalli kare tsarin.We mallaki cikakken sa na ci-gaba samar kwarara na refining, sanyi rage, zane da zafi jiyya da dai sauransu Mun kuma alfahari da m R&D iya aiki.
Ku rubuta sakonku anan ku aiko mana