Constantan Flat Waya Copper Nickel Alloy 6j40 Ribbon 0.4*2mm
Sabuwar Constantan Flat Waya Copper Nickel Alloy 6j11 Ribbon 0.4*2mm
| Halaye | Resistivity (200C μ Ω. m) | Max.Yanayin aiki (0C) | Ƙarfin Tensile (Mpa) | Matsayin narkewa (0C) | Yawan yawa (g/cm3) | TCR x10-6/0C (20 ~ 600 0C) | EMF vs Cu (μ V/ 0C) (0 ~ 100 0C) |
| Alloy Nomenclature | |||||||
| NC003 (CuNi1) | 0.1 | 200 | ≥ 250 | 1095 | 8.9 | < 100 | -12 |
| Abubuwan Jiki | Ma'auni | Sharhi |
| Yawan yawa | 8.94g/c | |
| Kayayyakin Injini | Ma'auni | Sharhi |
| Ƙarfin Ƙarfin Ƙarfi, Ƙarfi | 262-531 MPa | |
| Ƙarfin Ƙarfin Ƙarfin Ƙarfin Ƙarfafawa, Ƙarfafawa | 276-524 MPa | Dangane da fushi |
| Tsawaitawa a Break | 46.0% | da 50.8 mm. |
| Modulus na Elasticity | 115 GPA | |
| Rabon Poissons | 0.310 | Lissafi |
| Injin iya aiki | 20% | UNS C36000 (yankan tagulla kyauta) = 100% |
| Modulus Shear | 44.0 GPA | |
| Abubuwan Lantarki | Ma'auni | Sharhi |
| Resistivity na Lantarki | 0.0000120 ohm-cm @Zazzabi 20.0 ° C | |
| Thermal Properties | Ma'auni | Sharhi |
| CTE, layi | 17.5µ m/m-° C @Zazzabi 20.0 - 300 ° C | |
| Takamaiman Ƙarfin Zafi | 0.380 J/g-° C | |
| Thermal Conductivity | 64.0 W/mK @Zazzabi 20.0 ° C | |
| Matsayin narkewa | = 1125 ° C | Liquidus |
| Liquidus | 1125 ° C | |
| Abubuwan Gudanarwa | Ma'auni | Sharhi |
| Zazzabi mai zafi | 565-815 ° C | |
| Zazzabi-Aiki | 815-950 ° C | |
| Kayayyakin Abubuwan Abubuwan Abun Gaba | Ma'auni | Sharhi |
| Copper, Ku | > = 91.2% | |
| Irin, Fe | 1.30 - 1.70% | |
| Jagora, Pb | <= 0.050 % | |
| Manganese, Mn | 0.30 - 0.80% | |
| Nickel, Ni | 4.80 - 6.20% | |
| Zinc, Zan | <= 1.0% |
CuNi44 Abubuwan Sinadarai, %
| Ni | Mn | Fe | Si | Cu | Sauran | Umarnin ROHS | |||
| Cd | Pb | Hg | Cr | ||||||
| 44 | 1% | 0.5 | - | Bal | - | ND | ND | ND | ND |
Kayayyakin Injini
| Matsakaicin Yanayin Sabis na Ci gaba | 400ºC |
| Resistivity a 20ºC | 0.49± 5% ohm mm2/m |
| Yawan yawa | 8.9g/cm 3 |
| Thermal Conductivity | -6 (Max) |
| Matsayin narkewa | 1280ºC |
| Ƙarfin Ƙarfin Ƙarfin Ƙarfin Ƙarfafawa, N/mm2 Annealed, Mai laushi | 340 ~ 535 Mpa |
| Ƙarfin Ƙarfin Ƙarfin Ƙarfin Ƙarfin Ƙarfin Ƙarƙashin Ƙarƙashin Ƙarƙashin Ƙarƙashin Ƙarƙashin Ƙarƙashin Ƙarƙashin Ƙarƙashin Ƙarƙashin Ƙarƙashin Ƙarƙashin Ƙarƙashin Ƙarƙashin Ƙarƙashin Ƙarƙashin Ƙarƙashin Ƙarƙashin Ƙarƙashin Ƙarƙashin Ƙarƙashin Ƙarƙashin Ƙarƙashin Ƙarƙashin Ƙarƙashin Ƙarƙashin Ƙarƙashin Ƙarƙashin Ƙarƙashin Ƙarƙashin Ƙarƙashin Ƙarƙarar Ƙarƙarar Ƙarƙarar Ƙarƙarar Ƙarfafa Ƙarfin Ƙarƙarar Ƙarƙarar Ƙarfafa Ƙarfin Ƙarƙashin Ƙarƙashin Ƙarƙashin Ƙarƙashin Ƙarƙarar Ƙarƙarar Ƙarfafa Ƙarfin Ƙarfafa Ƙarfin Ƙarfafawa, N/mm3 Cold Rolled | 680 ~ 1070 Mpa |
| Tsawaita (anneal) | 25% (min) |
| Tsawaita (sanyi birgima) | ≥min) 2% (min) |
| EMF vs Cu, μV/ºC (0 ~ 100ºC) | -43 |
| Tsarin Micrographic | Austenite |
| Abubuwan Magnetic | Ba |