Astm TM2 Rxetal kintinkiri wanda aka yi amfani da shi don tsarin sarrafawa
Halayyar muhalli na ƙirar thermal tana canzawa tare da yanayin zafi da kuma kayan aikin zazzabi don samun tsarin sarrafawa ta atomatik da firikwensin yanayin zafin jiki a cikin kayan aikin.
| Alamar shagon | 5J1480 | |
| Tare da alama | 5J18 | |
| Hukumar alloybrand | Babban fadada fadada | Ni22cr3 |
| tsakiya na tsakiya | --- | |
| Lower ension Layer | Ni36 | |
Abubuwan sunadarai
| Alamar shagon | Ni | Cr | Fe | Co | Cu | Zn | Mn | Si | C | S | P |
| ≤ | |||||||||||
| Ni36 | 35.0 ~ 37.0 | - | izni | - | - | - | ≤0.6 | ≤0.3 | 0.05 | 0.02 | 0.02 |
| Ni22cr3 | 21.0 ~ 23.0 | 2.0 ~ 4.0 | izni | - | - | - | 0.3 ~ 0.6 | 0.15 ~ 0.3 | 0.25 ~ 0.35 | 0.02 | 0.02 |
cika
| Fiye da tanadi k (20 ~ 135ºC) | Tsarin zafin jiki Curvature F / (Greenhouse ~ 130 ºC) | jure wa | Linear zazzabi / ºC | Yana ba da damar amfani da zazzabi / ºC | Density (g / cm bayan) | |||
| Darajar maras muhimmanci | Bai dace karkacewa | Misali dabi'u | Bai dace karkacewa | |||||
| Mataki na 1 | Mataki na 2 | |||||||
| 14.3 | ± 5% | ± 7% | 26.2% ± 5% | 0.8 | ± 5% | -20 ~ 180 | -70 ~ 350 | 8.2 |
| Modulus na elalation E / GPA | Hardness (HV) | Da tenerile MPA | Bada izinin damuwa MPA | ||
| Babban fadada fadada | Lower ension Layer | m | babba | ||
| 147 ~ 177 | 270 ~ 340 | 200 ~ 255 | 785 ~ 883 | 196 | 343 |