Kasar China Feni Nickel Iron Syoy Tanuki

Feni Nickel Iron AlLoy 0.5m WireSe 0.5mm Warry Waya 36 Waya don rufe madaidaicin kayan aikin da aka sanya

Feni Nickel Iron AlLoy 0.5m Wurin 0.5mm Warry Waya 36 Waya don Saka Albarka

A takaice bayanin:

Model No .:Wire gyaran waya 36

Abu:Fe- ni alloy

Farfajiya:Santsi da haske

Yanayi:Taushi, 1 / 2h. M

Diamita:0.02- 5.0mm

Lambar HS:75125000

Yankuna (g / cm3):8.1

Aika imel zuwa gare mu

Cikakken Bayani

Faq

Tags samfurin

Feni Nickel Iron AlLoy 0.5mmWire gyaran waya 36Don hatimin kayan aiki

Haɗin kai 36Abin farin ciki ne, baƙin ƙarfe, low fadada riguna dauke da 36% nickel. Yana kula da kusan sauƙin yanayin yanayin zafi na yau da kullun na yau da kullun zuwa kimanin yanayin zafi zuwa kusan 500 ° F. The Alloy kuma yana riƙe da kyakkyawar ƙarfi da kuma tauri a yanayin zafi.

Haɗin kai 36na iya zama mai zafi da sanyi da aka kafa kuma mura ta amfani da tsari mai kama da

Ausenitic bakin karfe. Harry 36 ana weldable ta amfani da karfe mai narkewa Cf36 wanda yake

Akwai shi a cikin waya da yawa don duka GTAW da tsarin gudanarwa.

Abubuwan sunadarai

kayan haɗin kai	%	Fe	Ni	Mn	C	P	S	SI
wadatacce	min	Bal	35.0	0.2
wadatacce	max	Bal	37.0	0.6	0.05	0.02	0.02	0.3

Properties na jiki

Density (g / cm3) 8.1

Tsorewa na lantarki a 20ºC (MM2 / M) 0.78

Ruwa ya haifar da tsayayya da (20ºC ~ 200ºC) x10-6 / ºC 3.7 ºC 3.7 º 3.9

Yin aiki, λ / w / w / (m * ºC) 11

Curie Penty TC / ºC 230

Modulus na zamani, E / GPa 144

Melting Point ºC 1430

Ingantacciyar hanyar fadada

θ /c	α1 / 10-6ºC-1	θ /c	α1 / 10-6ºC-1
20 ~ -60	1.8	20 ~ 250	3.6
20 ~ -40	1.8	20 ~ 300	5.2
20 ~ -20	1.6	20 ~ 350	6.5
20 ~ -0	1.6	20 ~ 400	7.8
20 ~ 50	1.1	20 ~ 450	8.9
20 ~ 100	1.4	20 ~ 500	9.7
20 ~ 150	1.9	20 ~ 550	10.4
20 ~ 200 200	2.5	20 ~ 600	11.0

Kayan aikin kayan aikin yau da kullun

Da tenerile	Elongation
MPA	%
641	14
689	9
731	8

Yanayin zafi naRmisali

Kewayuwar zazzabi, ºC	20 ~ 50	20 ~ 100	20 ~ 200 200	20 ~ 300	20 ~ 400
Ar / 103 * ºC	1.8	1.7	1.4	1.2	1.0

Tsarin magani mai zafi
Annealing don kwanciyar hankali	Mai zafi zuwa 530 ~ 550 ~ 550 ọc kuma riƙe 1 ~ 2 h. Sanyi ƙasa
shafewa	Don kawar da hardening, wanda ya fito dashi a cikin sanyi-birgima, sanyi zane. Annealing yana buƙatar mai zafi zuwa 830 ~ 880ºC a cikin wuri, riƙe mintina 30.
Tsarin aiwatarwa	A kafofin watsa labarai masu kariya da mai zafi zuwa 830 ºc, riƙe 20min. ~ 1h, Quench Saboda wahalar da aka samar ta hanyar quenching, mai zafi zuwa 315ºC, riƙe 1 ~ 4h.
Matakan kariya	Ba zai iya zama taurarin zafi ba Jiyya na iya zama sandblasting, polished ko pickling. Za'a iya amfani da Alloy 25% Hydrochloric Acidar Acidar Acila a 70 ºC don share oxidized surface