42hxtio 3j53 Ni SpanC902 Spring Dindindin Magnetic Alloy
Daidaitaccen sassa na roba Material

Kauri na Takarda: 0.1mm ~ 3.5mm

Kauri na Faranti: 3.5mm ~ 40.0mm
Bar Dia 5.0mm ~ Dia180.0mm

Bututu OD 120mm~8.0mm, ID 8.0~129mm

Dia na Waya 0.1mm-Dia5.0mm

Aikace-aikacen Samfuran

Yawanci ana amfani da su don yin kayan aiki, gabobin ji mara waya, bellows, da diaphragms.

Bayani

Haɗin Nickel-Iron-Chromium mai taurarewa yana da kyakkyawan ma'aunin thermoelastic mai sarrafawa
halaye da kuma kyakkyawan juriya ga iskar shaka a yanayin zafi mai zafi. Ana iya sarrafa ƙarfen
don samun daidaitaccen tsarin sassauci a yanayin zafi tsakanin -45 zuwa +65oC (-50 zuwa +150oF).

Sigogi
TABLE 1 Bayani game da giciye

Sunan Yankin 1 Suna 2

Rasha 42HXTΙΟ H42XT

USA Ni-Span c902 Elinvar

Jamus Ni-Span C

UK Ni-Span C

Japan Sumispan-3 EL-3

TABLE 2 Bukatar Sinadarai

Haɗin Sinadaran,%

C ≤ 0.05

Si≤ 0.80

P≤ 0.020

S≤ 0.020

Mn≤ 0.80

Ni≤ 41.5-43.0

Cr 5.20-5.80

TI 2.3-2.70

Al 0.5-0.8

ragowar FE

Bayanan kula:

1. Siffa da girman ƙarfen sun yi daidai da YB/T5256-1993

TABLE 3 Bukatar Jiki

Manufar Kadara

Yawan yawa 8.0

Modulus na Ƙarfafawa (E/Empa) 176500-191000

Ƙarfin yankewa (G/MPa) 63500-73500

Taurin Vickers (HV) 350-450

Yawan shigar da ƙarfi (B600/T) 0.7

Matsakaicin Ma'aunin Faɗaɗawa Mai Layi20-100ºC(10-6/K) 8.5

Juriyar juriya p/(Ω°m) 1.1

TABBI NA 4 Ƙarfin Samar da Ƙarfi (bayan maganin zafi)

Kauri/mm Ƙarfin Yawa/Mpa na Jiha na Isarwa

An haɗa 0.50-2.50 <685

Sanyi birgima 0.50-1.00 >885

TABLE 5 Ma'aunin zafin jiki na modulus na elasticity

Zafin Tsufa/ºC Ma'aunin zafin jiki na modulus na elasticityβE/(10-6/ºC)(-6~+80ºC)

An Yi Murfin Sanyi Mai Sanyi

500 -38~15 +18~+12

550 -22~0 +10~+35

600 0~+20 +35~+55

650 0~+20 +42~+64

700 0~+20 +40~+60

750 -4~+16 +28~+50

TABBI NA 6 Bukatar kadarorin injina

Siffar Isarwa Jiha Kauri&Diamita/mm Ƙarfin Tensile/MPa Elongationò(%)≥

An haɗa shi da tsiri 0.20-0.50 <885 20
Waya Mai Sanyi 0.20-3.0 >930